Aluminothermic processing of mill scale to obtain iron alloys and abrasive and refractory slags.

Abstract

The mill scale is a residue that is continuously generated during the hot rolling process, constituting approximately 2% of the Steel produced, which is very little used in Cuba. In the present work, the obtaining of iron alloys and abrasive and refractory products through Aluminothermic processing is studied. For the conformation of the mixtures, a Mc Lean Anderson – type design of experiments is carried out, where the dependent variables are the mill scale, aluminum shavings and limestone. In this way, 7 loads were formed, which were processed in a graphite reactor, obtaining the corresponding alloys and slags. The alloys obtained are fundamentally composed of: carbon of 0.3 – 1.26%, silicon of 0.3 – 1.61%, manganese 0.3 – 0.96% and aluminum of 0.25 – 1.88%, with a recovery of the metal between 73 – 91% and of slags between 93 – 110%.

Resumen

La cascarilla de laminación es un residuo que se genera continuamente durante el proceso de laminación en caliente, constituyendo aproximadamente el 2% del acero producido, el cual es muy poco utilizado en Cuba. En el presente trabajo se estudia la obtención de aleaciones de hierro y de productos abrasivos y refractarios mediante procesamiento aluminotérmico. Para la conformación de las mezclas se realiza un diseño de experimentos de tipo Mc Lean Anderson, donde las variables dependientes son la cascarilla de laminación, virutas de aluminio y caliza. De esta manera se conformaron 7 cargas, las que se procesaron en un reactor de grafito, obteniéndose las correspondientes aleaciones y escorias. Las aleaciones obtenidas están integradas fundamentalmente por: carbono de 0.3 – 1.26%, silicio de 0.3 – 1.61%, manganeso 0.3 – 0.96% y aluminio de 0.25 – 1.88%, con una recuperación del metal entre 73 – 91% y de escoria entre 93 – 110%.