13rd International Symposium on Structures, Geotechnics and Construction Materials
2nd International Workshop on the production and sustainable use of cement and concrete
Abstract
The objective of the work was to study the granulometric fractions of white slag from the Las Tunas Stainless Steel Company (ACINOX Las Tunas) for use as supplementary cementitious material (MCS). This material was separated into fractions using standardized sieves, its chemical and mineralogical composition was determined using X-ray Diffraction and Atomic Absorption Spectroscopy techniques respectively. The white slag from the ladle furnace of the ACINOX Las Tunas electric steel mill is mainly formed by silicates, these are basic and the granulometry is mainly fine, with particles smaller than -0.044 mm predominating. This material has great prospects for its use as a partial substitute for cement or as a base for the development of new binders with pozzolanic additions.
Resumen
El trabajo tuvo como objetivo estudiar las fracciones granulométricas de las escorias blancas de la Empresa de Aceros Inoxidables de Las Tunas (ACINOX Las Tunas) para su empleo como material cementicio suplementario (MCS). Este material fue separado en fracciones usando tamices normados, se determinó su composición química y mineralógica mediante técnicas de Difracción de Rayos X y Espectroscopía de Absorción Atómica respectivamente. Las escorias blancas del horno de cuchara de la acería eléctrica ACINOX Las Tunas están formadas principalmente por silicatos, estas son básicas y la granulometría es principalmente fina, predominando partículas inferiores a -0.044 mm. Este material presenta grandes perspectivas para su empleo como sustituto parcial del cemento o como base para el desarrollo de nuevos conglomerantes con adiciones puzolánicas
About The Speaker
MsC. Angel Eduardo Espinosa Borges
Discussion